合金牌号 |
状态 |
力学性能 |
化学成分 | |||||||||||
抗拉 强度 |
屈服 强度 |
延伸率 |
硬度 |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Pb |
Bi | ||
Mpa |
% |
HW |
|
|
|
|
|
|
|
|
| |||
2014 |
T4 |
375 |
210 |
16 |
|
0.60-1.0 |
0.50 |
4.1-4.9 |
0.60-1.0 |
0.40-0.70 |
0.10 |
0.25 |
|
|
T6 |
400 |
340 |
12 |
| ||||||||||
5083 |
H112 |
270 |
110 |
12 |
|
0.40 |
0.40 |
0.10 |
0.50-0.90 |
4.0-4.9 |
0.05-0.25 |
0.25 |
|
|
H113 |
285 |
185 |
12 |
| ||||||||||
6005 |
T1 |
170 |
105 |
16 |
9 |
0.60-0.90 |
0.35 |
0.10 |
0.10 |
0.40-0.60 |
0.10 |
0.10 |
|
|
T5、T6 |
260 |
240 |
10 |
15 | ||||||||||
|
T1 |
170 |
100 |
15 |
9 |
0.55-0.85 |
0.35 |
0.30 |
0.40 |
0.40-0.70 |
0.30 |
0.20 |
|
|
T4 |
180 |
110 |
14 |
9.5 | ||||||||||
T5 |
260 |
215 |
7 |
15 | ||||||||||
T6 |
270 |
225 |
8 |
15.5 | ||||||||||
6060 |
T1 |
115 |
60 |
12 |
5 |
0.35-0.55 |
0.10-0.30 |
0.1. |
0.10 |
0.35-0.50 |
0.05 |
0.15 |
|
|
T5 |
150 |
110 |
8 |
7.5 | ||||||||||
T52 |
150-205 |
7.5-11 | ||||||||||||
6061 |
T1 |
180 |
95 |
16 |
9.5 |
0.50-0.80 |
0.55 |
0.20-0.40 |
0.15 |
0.80-1.0 |
0.04-0.2 |
0.25 |
|
|
T4 |
180 |
110 |
14 |
9.5 | ||||||||||
T51 |
240 |
205 |
8 |
13.5 | ||||||||||
T6 |
260 |
240 |
8 |
15 | ||||||||||
6063 |
T1 |
115 |
60 |
12 |
5 |
|
|
|
|
|
|
|
|
|
T4 |
130 |
70 |
6 |
|
|
|
|
|
|
|
|
| ||
T5 |
160 |
110 |
8 |
8 |
0.30-0.55 |
0.35 |
0.10 |
0.10 |
0.40-0.65 |
0.10 |
0.10 |
|
| |
T52 |
150-205 |
110-173 |
8 |
7.5-11 | ||||||||||
T6 |
205 |
180 |
8 |
11 | ||||||||||
|
T5 |
200 |
160 |
5 |
11 |
0.35-0.55 |
0.35 |
0.10 |
0.15 |
0.65-0.85 |
0.05 |
0.15 |
|
|
T6 |
230 |
190 |
5 |
13 | ||||||||||
6082 |
T4 |
205 |
110 |
14 |
11 |
0.80-1.1 |
0.40 |
0.10 |
0.45-0.80 |
0.75-1.1 |
0.25 |
0.20 |
|
|
T5 |
270 |
230 |
8 |
15.5 | ||||||||||
T6 |
310 |
260 |
8 |
18.5 | ||||||||||
6106 |
T4 |
130 |
70 |
12 |
6 |
0.30-0.50 |
0.35 |
0.30 |
0.40 |
0.40-0.70 |
0.30 |
0.20 |
|
|
T5 |
|
|
|
| ||||||||||
T6 |
235 |
210 |
8 |
13 | ||||||||||
T832 |
275-310 |
240-265 |
10 |
16-18 | ||||||||||
6262 |
T6 |
260 |
240 |
10 |
15 |
0.50-0.70 |
0.40 |
0.20-0.35 |
0.15 |
0.90-1.1 |
0.04-0.12 |
0.25 |
0.45-0.65 |
0.45-0.65 |
T6511 |
289 |
17 | ||||||||||||
6463 |
T1 |
115 |
60 |
12 |
5 |
0.30-0.55 |
0.15 |
0.10 |
0.10 |
0.40-0.65 |
0.05 |
0.05 |
|
|
T5 |
150 |
110 |
8 |
7.5 | ||||||||||
T6 |
205 |
170 |
8 |
11 | ||||||||||
7005 |
T53 |
345 |
303 |
10 |
21 |
0.25 |
0.30 |
0.10 |
0.30-0.50 |
1.30-1.60 |
0.06-0.15 |
4.0-5.0 |
Zr 0.12-0.14 |
|
7075 |
T73 |
470 |
400 |
7 |
|
0.30 |
0.35 |
1.4-1.8 |
0.30 |
2.3-2.8 |
0.18-0.28 |
5.1-6.1 |
|
|